Recent Progress in Two-Dimensional MoTe2 Hetero-Phase Homojunctions

With the demand for low contact resistance and a clean interface in high-performance field-effect transistors, two-dimensional (2D) hetero-phase homojunctions, which comprise a semiconducting phase of a material as the channel and a metallic phase of the material as electrodes, have attracted growing attention in recent years. In particular, MoTe2 exhibits intriguing properties and its phase is easily altered from semiconducting 2H to metallic 1T′ and vice versa, owing to the extremely small energy barrier between these two phases. MoTe2 thus finds potential applications in electronics as a representative 2D material with multiple phases. In this review, we briefly summarize recent progress in 2D MoTe2 hetero-phase homojunctions. We first introduce the properties of the diverse phases of MoTe2, demonstrate the approaches to the construction of 2D MoTe2 hetero-phase homojunctions, and then show the applications of the homojunctions. Lastly, we discuss the prospects and challenges in this research field.


Introduction
Over the past few years, the complexity of integrated circuits (IC) in the semiconductor industry has increased with the decrease in the size of components [1,2]. However, traditional silicon-based transistors have been confronted with fundamental limits induced by quantum mechanics and thermodynamics at the nanometer scale [3], thereby leading to several problems, such as the short-channel effect [4,5] and severe carrier scattering by surface dangling bonds [6,7], which would degrade the device performance and hinder the scaling. To solve these problems, low-dimensional electronic materials including transition metal dichalcogenides (TMDs) have been intensively studied due to their prominent advantages, including atomically thin thickness without dangling bonds, diversity of bandgaps, and excellent performance that is superior to their silicon counterparts [8]. For an ideal 2D transistor, there are four essential elements, which are a high-mobility 2D semiconductor channel, a high-κ dielectric, an ultrasmooth substrate with high thermal conductance, and ohmic contacts with low Schottky barrier height (SBH) [9] and low contact resistance [8]. Thus far, it remains challenging to realize ohmic contacts with ultralow SBH [10] because of the large energy difference between the semiconductor electron affinity and the metal work function, as well as Fermi-level pinning resulting from metal-induced gap states (MIGS) [11][12][13]. Moreover, in the conventional device fabrication process involving multistep procedures, 2D electronic devices are vulnerable to defects and impurities, leading to a deterioration in their performance.
Two-dimensional hetero-phase homojunctions provide a solution to these problems. Multiple phases of some TMDs [14] allow us to construct circuits composed of the metallic phase as electrodes or interconnects and the semiconducting phase as channels, which avoids external metal contacts and unnecessary film depositions [15]. Moreover, with careful selection of the appropriate materials, the SBH between the hetero-phases is expected to be ultralow if the interface is covalently bonded and atomically coherent [16].  [24] 2016 Springer Nature; (e) Raman spectra of 2H-, 1T′-, and Td-MoTe2, Reprinted with permission from [18] 2019 American Chemical Society.
In this review, we summarize the recent progress in 2D MoTe2 hetero-phase homojunctions. First, we introduce the properties of three phases of MoTe2, namely the 2H, 1T′, and Td phases [28]. Second, the strategies for constructing 2D MoTe2 hetero-phase homojunctions are demonstrated regarding two aspects, direct synthesis and post-processing. Next, we manifest applications of 2D MoTe2 hetero-phase homojunctions in electronics, optoelectronics, and catalysis. Finally, we discuss the current challenges and opportunities in this research field. In this review, we summarize the recent progress in 2D MoTe 2 hetero-phase homojunctions. First, we introduce the properties of three phases of MoTe 2 , namely the 2H, 1T , and T d phases [28]. Second, the strategies for constructing 2D MoTe 2 hetero-phase homojunctions are demonstrated regarding two aspects, direct synthesis and post-processing. Next, we manifest applications of 2D MoTe 2 hetero-phase homojunctions in electronics, optoelectronics, and catalysis. Finally, we discuss the current challenges and opportunities in this research field.

Phases and Properties of MoTe 2
Near room temperature, MoTe 2 exhibits three stable phases: 2H, 1T , and T d phases. These phases have different lattice structures, band structures, and fingerprints in optical spectra.

2H Phase
As shown in Figure 1a, 2H-MoTe 2 (α-phase) exhibits a hexagonal structure, and it belongs to the space group P6 3 /mmc with a honeycomb-like in-plane structure [28]. In addition, 2H-MoTe 2 is an indirect bandgap semiconductor (bandgap 0.8 eV [29]) in bulk and few-layer states (Figure 1c). When thinned to a monolayer, however, it becomes a direct bandgap semiconductor (bandgap 1.1 eV [30]). Generally, 2H-MoTe 2 is relatively stable in ambient conditions, but, due to the extremely small energy barrier with 1T -MoTe 2 , it will convert into the 1T phase under excess Te deficiency or strain [31,32].

1T Phase
Firstly, 1T -MoTe 2 (β-phase) has a monolithic structure, belonging to space group P2 1 /m, with a distorted centered honeycomb in-plane structure and slightly inclined interplane structure (β angle = 93 • 55 ) [28], as shown in Figure 1a. Compared to 2H-MoTe 2 , 1T -MoTe 2 is more vulnerable to oxidation [33]. In addition, 1T -MoTe 2 is generally acknowledged to be metallic, whether in the bulk or monolayer state. However, there are some reports designating few-layer 1T -MoTe 2 as a semiconductor. Keum et al. reported that few-layer 1T -MoTe 2 exhibited a bandgap opening up to 60 meV ( Figure 1c) and proposed that it was induced by strong spin-orbit coupling (SOC) [17]. More recently, tri-layer 1T -MoTe 2 was reported to possess a narrow bandgap of 28 meV, but, in thicker MoTe 2 samples (>4 nm), such bandgap opening was not observed [34]. On the contrary, it was also reported that tri-layer 1T -MoTe 2 remained free of a bandgap [35]. It is still under debate whether few-layer 1T -MoTe 2 has a bandgap.
In addition, 1T -MoTe 2 was reported to be a topological insulator as well as a roomtemperature ferroelectric material. A weak antilocalization effect was observed in monolayer 1T -MoTe 2 , indicating the presence of strong SOC, which is related to topological insulator materials [22]. Bulk 1T -MoTe 2 was predicted to be a Z4-nontrivial higher-order TI (HOTI) driven by double band inversion [23], which has not been experimentally confirmed yet. Recently, robust room-temperature out-of-plane ferroelectricity was observed in monolayer distorted 1T-MoTe 2 [36], which has sparked the exploration of fundamental physics and promising applications at the monolayer limit.

T d Phase
T d -MoTe 2 (γ-phase) has an orthogonal structure, belonging to space group Pmn2 1 [28]. Compared to the 1T phase, the T d phase displays a very similar but more regular structure (Figure 1a). From the cross-section direction, atoms in different layers of T d -MoTe 2 are in good alignment with each other, whereas, in 1T -MoTe 2 atoms, layers slide a short distance and form a 0.94 • tilt angle. Therefore, it is almost impossible to distinguish 1T from T d MoTe 2 at the level of the monolayer.
When the temperature is increased above~250 K, the T d phase is supposed to convert to the 1T phase [37]. In order to obtain stable T d -MoTe 2 at room temperature, tungsten substitutional doping [38] and thinning the material to be below 10 nm [37,39] are effective strategies. Owing to its broken inversion symmetry, the T d phase possesses abundant physical properties, such as superconductivity and Type-II WSM.
T d -MoTe 2 exhibits pressure-and thickness-dependent superconductivity. The transition temperature T c of T d -MoTe 2 increases with higher pressure and smaller thickness. The T c of bulk T d -MoTe 2 was reported to be 0.10 K (Figure 1d) [24]. Guguchia et al. observed the two-gap s-wave symmetry of the superconducting order parameter in T d -MoTe 2 , and suggested a higher possibility of a topologically non-trivial s +− state in T d -MoTe 2 [40]. A fast-mode oscillation of the critical current I c versus magnetic field B along the edge was observed in T d -MoTe 2 by Wang et al., which was generated by fluxoid quantization and indicated the existence of a robust edge supercurrent [41]. As the breaking of the time-reversal symmetry or inversion symmetry is the prerequisite for WSM, T d -MoTe 2 was predicted as a Type-II WSM due to its noncentrosymmetric lattice structure [26]. Kaminski et al. identified Fermi arcs, Weyl points, and novel surface states in bulk T d -MoTe 2 with the angle-resolved photoemission spectroscopy (ARPES) technique, providing experimental evidence for T d -MoTe 2 as a Type-II WSM [42]. Large magnetoresistance, a chiral-anomaly-related phenomenon, was reported in T d -MoTe 2 , further proving that T d -MoTe 2 is a representative Type-II WSM [43,44].

Direct Synthesis
Chemical vapor deposition (CVD) is a universal and convenient method for the direct synthesis of 2D materials and heterojunctions, which is also viable in the case of MoTe 2 hetero-phase homojunctions. The key to constructing 2D MoTe 2 hetero-phase homojunctions is precise control of phases. The final phase of MoTe 2 after growth is determined by several factors, which are growth temperature, growth atmosphere, and Te vacancy concentration.
It was reported that the most thermodynamically stable phase varied under different processing temperatures [45]. Thus, by controlling the growth temperature, a certain phase can be selectively obtained. Sung et al. reported that the 1T -phase was the dominant product at a higher temperature (710 • C), and the 2H phase dominated at a lower temperature (670 • C) [16]. By sequential growth of 1T and 2H-MoTe 2 , they obtained isolated lateral 1T -2H-MoTe 2 homojunctions (Figure 2a). With increasing temperature, Yang et al. observed the phase evolution shown in Figure 2c: pure 1T -phase→1T -and 2H-phase→pure 2H-phase→2H-and 1T -phase→pure 1T -phase [46].
Besides the growth temperature, the growth atmosphere plays an important role in controlling the phases in MoTe 2 . By changing the flow rate of either the inert carrier gas (N 2 ) or active carrier gas (H 2 ), phase evolutions with a tendency similar to the aforementioned were reported [46,47]. Such phase evolution was attributed to the tellurization velocity, and conclusions were drawn that a fast tellurization velocity favored 1T phase formation, while a moderate tellurization velocity favored the 2H phase [46]. It is possibly analogous to the formation of dendrites, wherein a fast cooling rate leads to plenty of dendrites, which possess a more disordered and defect-rich structure, while a moderate cooling rate results in a more regular and thermodynamically stable structure.
In essence, the process of phase transition in MoTe 2 is structural transformation [48], which can be triggered by either external stimuli, such as temperature and growth rate, or internal factors such as strain and Te deficiency. The influence of strain in the phase control of MoTe 2 will be discussed in the next section. The utility of the Te deficiency in the phase control of MoTe 2 has been intensively studied. It was reported that the 1T phase of MoTe 2 was more stable than the 2H phase when the Te deficiency exceeded 2%, which was confirmed by density functional theory (DFT) calculations [48]. In CVD synthesis, the concentration of Te deficiency is tunable by controlling the concentrations or compositions of precursors.
Strategies such as prolonging the growth time [49], increasing Te atomic flux by raising the source temperature ( Figure 2b) [50], and controlling the concentration of MoO 3 precursor by means of molecular sieves and overlapped substrates [51] were proven to be effective to provide excessive Te during the growth period and thereby obtain the stable stoichiometric 2H phase. Accordingly, the reverse phase transition from 2H to 1T -MoTe 2 could be realized by further annealing under a lower partial pressure of Te at the same temperature, followed by rapid quenching [49]. Moreover, a mixed-dimensional in-plane 1D-2D Mo 6 Te 6 -MoTe 2 heterostructure was directly synthesized under medium Te flux [52]. Besides the growth temperature, the growth atmosphere plays an important role in controlling the phases in MoTe2. By changing the flow rate of either the inert carrier gas (N2) or active carrier gas (H2), phase evolutions with a tendency similar to the aforementioned were reported [46,47]. Such phase evolution was attributed to the tellurization velocity, and conclusions were drawn that a fast tellurization velocity favored 1T′ phase formation, while a moderate tellurization velocity favored the 2H phase [46]. It is possibly analogous to the formation of dendrites, wherein a fast cooling rate leads to plenty of dendrites, which possess a more disordered and defect-rich structure, while a moderate cooling rate results in a more regular and thermodynamically stable structure.
In essence, the process of phase transition in MoTe2 is structural transformation [48], which can be triggered by either external stimuli, such as temperature and growth rate, or internal factors such as strain and Te deficiency. The influence of strain in the phase control of MoTe2 will be discussed in the next section. The utility of the Te deficiency in the phase control of MoTe2 has been intensively studied. It was reported that the 1T′ phase of MoTe2 was more stable than the 2H phase when the Te deficiency exceeded 2%, which was confirmed by density functional theory (DFT) calculations [48]. In CVD synthesis, the concentration of Te deficiency is tunable by controlling the concentrations or compositions of precursors. By tellurizing precursors with different compositions, 2H and 1T -MoTe 2 were simultaneously synthesized by Zhang et al. [15]. The products after tellurizing MoO 2.0-2.5 and MoO 3 thin films were identified as 2H and 1T -MoTe 2 , respectively ( Figure 2d). The authors proposed that the selective phase synthesis was realized by the varied Te monovacancies densities in the products. Combining the above synthesis strategies with lithographic processes, 2D MoTe 2 hetero-phase junctions [50,53] and their derivatives, such as MoTe 2 field-effect transistor (FET) arrays [54,55] and integrated MoTe 2 circuits [15], were successfully fabricated.
Recently, Xu et al. showed that the structure of 2H-MoTe 2 could spread into the adjacent 1T phase under a Te-rich atmosphere [56]. Triggered by an implanted singleseed crystal, they synthesized wafer-scale single-crystalline 2H-MoTe 2 via 2D epitaxy of polycrystalline 1T -MoTe 2 .

Post-Processing
Besides direct synthesis, post-processing is also a very versatile strategy to realize 2D MoTe 2 hetero-phase homojunctions. Owing to the small energy barrier between the 2H and 1T phases, external stimuli, such as a laser, electrostatic gating, mechanical deformations, chalcogen alloying, and lithium-ion (Li + ) intercalation, can easily induce phase transition in MoTe 2 .
Laser treatment was reported to induce Te vacancies in MoTe 2 , which thereafter triggered the local phase transition from the 2H phase to 1T phase [57][58][59]. Cho et al. used laser-induced phase patterning to fabricate an ohmic 2H-1T hetero-phase homojunction that was stable up to 300 • C (Figure 3a) [57]. Not only an ohmic contact between phases but also a patterned phase transfer area could be achieved by this method. By carefully adjusting the laser power and irradiation time, the structural phases of MoTe 2 could be gradually controlled [60]. Similarly, a scanning visible light probe could be used to directly write electrical circuits onto 2H-MoTe2 thin films (Figure 3b) [61]. By creating adatom-vacancy clusters in the host lattice, laser light illumination on patterned metal deposited onto 2H-MoTe2 could locally convert the underneath area from an n-type semiconductor to a p-type semiconductor. This doping method could be utilized to assemble both n-and p-doped channels in the same atomic plane at the submicrometer scale, making it possible to fabricate 2D n-p-n (p-n-p) bipolar junction transistor amplifier arrays as well as radial p-n photovoltaic cells.
Electrostatic gating was expected to be a flexible and viable means of phase transition in MoTe2. Li et al. predicted the structural semiconductor-to-semimetal phase transition in monolayer MoTe2 induced by electrostatic gating [62]. In order to observe 2H-1T′ phase transition in undoped monolayer MoTe2 under the constant-stress circumstance, a surface charge density of <−0.04 e or >0.09 e per formula unit was found to be required. Employing Similarly, a scanning visible light probe could be used to directly write electrical circuits onto 2H-MoTe 2 thin films (Figure 3b) [61]. By creating adatom-vacancy clusters in the host lattice, laser light illumination on patterned metal deposited onto 2H-MoTe 2 could locally convert the underneath area from an n-type semiconductor to a p-type semiconductor. This doping method could be utilized to assemble both n-and p-doped channels in the same atomic plane at the submicrometer scale, making it possible to fabricate 2D n-p-n (p-n-p) bipolar junction transistor amplifier arrays as well as radial p-n photovoltaic cells.
Electrostatic gating was expected to be a flexible and viable means of phase transition in MoTe 2 . Li et al. predicted the structural semiconductor-to-semimetal phase transition in monolayer MoTe 2 induced by electrostatic gating [62]. In order to observe 2H-1T phase transition in undoped monolayer MoTe 2 under the constant-stress circumstance, a surface charge density of <−0.04 e or >0.09 e per formula unit was found to be required. Employing a capacitor structure (Figure 3c), a gate voltage of 2-4 V was required to dynamically control the 2H-1T phase transition in monolayer MoTe 2 (Figure 3d). In addition, alloying was predicted to effectively reduce the transition gate voltage-for example, down to 0.3-1 V for Mo x W 1−x Te 2 monolayers.
As is mentioned above, lattice distortion can also lead to structural transition in MoTe 2 . Duerloo et al. predicted that mechanical deformations could induce phase transition between a semiconducting and a metallic crystal structure in Mo-and W-dichalcogenide monolayers (Figure 3e), and identified that, under uniaxial conditions at room temperature, MoTe 2 required tensile strains ranging from 0.3 to 3% to have phase transition [63]. Subsequently, a room-temperature 2H-1T transition in a MoTe 2 thin film induced experimentally by a tensile strain of 0.2% was reported [64]. A 2H-MoTe 2 thin film was transferred to a patterned Si/SiO 2 substrate with cavities of different diameters, and the researchers then introduced tensile strain using an atomic force microscope (AFM) tip. The supported area without strain remained semiconducting, the suspended area exhibited metallic properties, and the peripheral area displayed both 1T and 2H Raman signals. After the release of the strain, the semiconductor-metal phase transition at room temperature was found to be reversible under ambient conditions, which was attributed to the large volume change and small latent heat during the phase transition.
Chalcogen alloying was first introduced to assist electrostatic gating by significantly reducing the transition gate voltage, but, later, alloying alone was found to effectively control the phases of MoTe 2 . Duerloo et al. predicted the structural phase transitions of alloyed MoTe 2 -WTe 2 monolayers with phase transition temperatures ranging from 0 to 933 K, and mapped its temperature-composition phase diagrams by DFT calculations [65].  (Figure 3f), which exhibited a semiconducting to semi-metallic transition as a function of x [38]. A small critical W concentration x c~8 % was reported to stabilize the γ-phase, which possessed a Fermi surface near that of WTe 2 at room temperature. The effect of chalcogen alloying on the energy difference and stability between the H and T phases in monolayer MoTe 2 was then studied by DFT calculations [67]. Seven MoTe 2−x X x alloys (X = N, P, Sb, F, Br, I, and Se) at three concentrations were investigated, and the energy difference between the H and T phases was found to be reliant on the chemistry, size, and concentration of the dopants. The p-type and n-type dopants were reported to contribute to defect states atop the valence band and states at the Fermi level of MoTe 2 , respectively.
Li + intercalation was predicted to be possible by DFT calculations to induce phase transition in MoTe 2 by intercalating Li + ions energetically stable on the 1T phase [68]. Utilizing a convection-assisted Li + intercalation method, Eshete et al. converted the surfaces of single-crystalline 2H-MoTe 2 into the 1T phase, and fabricated a vertical 1T -2H-1T MoTe 2 homojunction [69]. Such a vertical hetero-phase junction was expected to allow active charge transfer and provide numerous catalytic active sites, exhibiting great potential in electrochemical catalysis applications.

Electronic Devices
Transistors with ohmic contacts have always been in great demand in the semiconductor industry due to their high performance and low power consumption [70,71]. However, the external metal electrodes in transistors tend to induce not only high SBH, resulting from Fermi-level pinning, but also impurities and defects owing to the multi-step proce-dures of device fabrication, which leads to severe deterioration in device performance [72]. Two-dimensional MoTe 2 hetero-phase homojunctions provide a solution to these problems.
Owing to the small energy barrier between the metallic 1T phase and semiconducting 2H phase, the coexistence of the two phases is attainable in transistors as electrodes and channels, respectively. If covalently bonded and atomically coherent, the hetero-phase interface in MoTe 2 is anticipated to possess an ultralow SBH [16], which incidentally avoids contamination introduced by external metal contacts and unnecessary film depositions. Thus, there are high hopes for 2D MoTe 2 hetero-phase homojunctions in applications involving electronic devices.

Transistors
Transistors are the basic components of IC, where 2D MoTe 2 hetero-phase homojunctions have found their way towards high performance. Sung et al. found that the coplanar contacted 1T -2H MoTe 2 FETs outperformed conventional Au top-contacted FETs, with significantly higher gate tunability and on current (Figure 4a,b) [16]. By analyzing energy band diagram models and experimental results of the temperature-dependent conductance of FETs at various gate voltages V g , they found an ultralow SBH (~25 meV) of the atomically coherent 1T -2H MoTe 2 coplanar contact. Similar experimental results in lateral polymorphic MoTe 2 homojunction FETs fabricated by flux-controlled phase engineering were reported [15,54,73]. problems. Owing to the small energy barrier between the metallic 1T′ phase and semiconducting 2H phase, the coexistence of the two phases is attainable in transistors as electrodes and channels, respectively. If covalently bonded and atomically coherent, the hetero-phase interface in MoTe2 is anticipated to possess an ultralow SBH [16], which incidentally avoids contamination introduced by external metal contacts and unnecessary film depositions. Thus, there are high hopes for 2D MoTe2 hetero-phase homojunctions in applications involving electronic devices.

Transistors
Transistors are the basic components of IC, where 2D MoTe2 hetero-phase homojunctions have found their way towards high performance. Sung et al. found that the coplanar contacted 1T′-2H MoTe2 FETs outperformed conventional Au top-contacted FETs, with significantly higher gate tunability and on current (Figure 4a,b) [16]. By analyzing energy band diagram models and experimental results of the temperature-dependent conductance of FETs at various gate voltages Vg, they found an ultralow SBH (~25 meV) of the atomically coherent 1T′-2H MoTe2 coplanar contact. Similar experimental results in lateral polymorphic MoTe2 homojunction FETs fabricated by flux-controlled phase engineering were reported [15,54,74].  The mechanism of the reduced contact resistance in monolayer coplanar polymorphic MX 2 (MoS 2 , WS 2 , MoSe 2 , WSe 2 , MoTe 2 ) FETs with the 2H phase as channels and 1T phase as electrodes was demonstrated via ab initio quantum transport simulations [75]. MIGS at the interface was revealed to penetrate the Schottky barrier and connect the valence/conduction band of the channel and the electrodes, consequently leading to a tunable and lower effective SBH and an equivalent ohmic contact under a proper gate voltage. The electronic and contact properties of twelve interface structures of monolayer coplanar 2H-1T -MoTe 2 interfaces were investigated using first-principles calculations [76]. The two most energy-favored structures were named as (0 • , 30 • ) and (0 • , −30 • ), and the former was predicted to possess a small SBH, while the Fermi level of the latter was anticipated to be located near the midgap.
Taking advantage of the ultralow contact resistance in 2D MoTe 2 hetero-phase homojunctions, various applications based on polymorphic MoTe 2 transistors were exploitedfor example, MoTe 2 radiofrequency (RF) transistors with excellent air stability and a remarkable cutoff frequency (320 MHz with a 5 µm gate length), an ultrashort-gate-length 1T -2H-MoTe 2 FET based on a CNT gate with a small subthreshold swing (~73 mV dec −1 ) and a high on/off current ratio (~10 5 ), and three-dimensional IC by assembling layers of phase-patterned MoTe 2 [15].

Logical Devices
By tellurizing patterned different precursors, arrays of hetero-phase MoTe 2 logic inverters were prepared, which exhibited excellent logic-level conservation, good air stability, and eligibility for IC composed of multiple cascaded inverters (Figure 4c,d) [15]. Under the electric-field-induced strain generated by a ferroelectric substrate, Hou et al. observed the reversible phase transition between few-layer 1T and 2H-MoTe 2 in an FET geometry [73]. This new strategy for transistor switching circumvented the problems of static and dynamic power consumption in conventional FETs. They achieved large nonvolatile changes in channel conductivity between two states at room temperature (Figure 4g-i), indicating the great potential of the sub-nanosecond low-power non-volatile strain switching strategy for applications such as logic and memory devices.

Memory Devices
In vertical 2H-MoTe 2 /Mo 1−x W x Te 2 resistive random access memory (RRAM) devices, Zhang et al. reported an electric-field-induced phase transition from 2H to 2H d (a distorted transient structure) and the T d phase [29]. They achieved ultrafast, reproducible, resistive switching with on/off current ratios of 10 6 and programming currents lower than 1 µA in a selectorless RRAM architecture utilizing an Al 2 O 3 /MoTe 2 stack (Figure 4e,f).

Capacitors
Mixed-dimensional MoTe 2 structures have shown impressive potential in energy conversion applications. A supercapacitor based on an integrated structure of few-layer 2H-MoTe 2 and 1T -Mo 6 Te 6 nanoplates (NPs) was reported to exhibit enhanced areal capacitance (1542 mF cm −2 at 10 mV s −1 ) compared with a transferred monolayer mixed-dimensional electrode, as well as a high energy density (140.36 mW cm −2 at 4 mA) and excellent electrochemical stability (96%) [77]. This was attributed to the synergistic effect of 1D Mo 6 Te 6 NPs and 2D MoTe 2 layers in the integrated structure, which provided a large surface area and highly conductive pathway, enabling K + ions to diffuse effectively and favoring rapid reversible redox reactions.

Optoelectronic Devices
As is mentioned above, few-layer 2H-MoTe 2 possesses an indirect bandgap of 0.8 eV, which is suitable for near-infrared (NIR) photodetection [78]. The photogating effect was considered to dominate the photocurrent generation in few-layer 2H-MoTe 2 -based photodetectors and the detailed mechanism was demonstrated as follows: after the generation of electron-hole pairs under irradiation, the charged trap states in the channel acted as a local floating gate and induced more electrons by trapping holes, leading to effective tuning of the channel conductance [79,80].
For MoTe 2 hetero-phase homojunctions, photodetectors with both lateral and vertical structures were reported. Via a two-step patterned CVD growth and transfer method, Xu et al. fabricated a lateral 1T -2H-1T -MoTe 2 hetero-phase FET array on a flexible polyimide substrate [54]. They measured the NIR photoresponsivity of the hetero-phase photodetector under different incident light powers and showed a high NIR photoresponsivity of~1.02 A/W (Figure 5a-c). Lin et al. constructed a vertical 1T -2H-MoTe 2 hetero-phase photodetectors and compared the optical response properties to that without inserting 1T -MoTe 2 interlayer contact [81]. considered to dominate the photocurrent generation in few-layer 2H-MoTe2-based photodetectors and the detailed mechanism was demonstrated as follows: after the generation of electron-hole pairs under irradiation, the charged trap states in the channel acted as a local floating gate and induced more electrons by trapping holes, leading to effective tuning of the channel conductance [79,80]. For MoTe2 hetero-phase homojunctions, photodetectors with both lateral and vertical structures were reported. Via a two-step patterned CVD growth and transfer method, Xu et al. fabricated a lateral 1T′-2H-1T′-MoTe2 hetero-phase FET array on a flexible polyimide substrate [54]. They measured the NIR photoresponsivity of the hetero-phase photodetector under different incident light powers and showed a high NIR photoresponsivity of ~1.02 A/W (Figure 5a-c). Lin et al. constructed a vertical 1T′-2H-MoTe2 hetero-phase photodetectors and compared the optical response properties to that without inserting 1T′-MoTe2 interlayer contact [81].

Electrocatalysis Materials
Furthermore, 1T′-MoTe2 was reported to have significant potential in electrocatalysis. Resulting from the adsorption of H atoms onto Te sites on the surface, 1T′-MoTe2 exhibited a rapid and reversible activation process where the overpotential required to maintain a certain current density decreased significantly when held at cathodic bias [83].
Chen et al. illustrated that 2H-1T′ phase boundaries could effectively activate the basal plane of monolayer MoTe2 for enhanced hydrogen evolution reaction (HER) performance [82]. They investigated, by first-principles calculations, the structural and energetics stabilities of possible configurations of the 2H-1T′ phase boundary, including Te, Mo, and hollow sites, which were identified as possible catalytic centers for the HER at ener-

Electrocatalysis Materials
Furthermore, 1T -MoTe 2 was reported to have significant potential in electrocatalysis. Resulting from the adsorption of H atoms onto Te sites on the surface, 1T -MoTe 2 exhibited a rapid and reversible activation process where the overpotential required to maintain a certain current density decreased significantly when held at cathodic bias [83].
Chen et al. illustrated that 2H-1T phase boundaries could effectively activate the basal plane of monolayer MoTe 2 for enhanced hydrogen evolution reaction (HER) performance [82]. They investigated, by first-principles calculations, the structural and energetics stabilities of possible configurations of the 2H-1T phase boundary, including Te, Mo, and hollow sites, which were identified as possible catalytic centers for the HER at energetically stable phase boundaries (Figure 5d). In particular, the hollow sites newly induced by phase boundaries exhibited comparable Gibbs free energy to that of Pt near the thermoneutral value for H 2 adsorption (Figure 5e), which was due to the unique electronic structures and local geometries of H 2 adsorption at phase boundaries.

Summary and Prospects
In this short review, we summarized the recent progress in 2D MoTe 2 hetero-phase homojunctions. We first briefly introduced the properties of three phases of MoTe 2 , namely the 2H, 1T , and T d phases, and then illustrated two strategies, direct synthesis and postprocessing, to construct 2D MoTe 2 hetero-phase homojunctions. We also enumerated the applications of 2D MoTe 2 hetero-phase homojunctions in electronics, optoelectronics, and electrocatalysis.
Despite the fascinating prospects, 2D MoTe 2 hetero-phase homojunctions are confronted with several challenges. First, the synthesis and characterization of monolayer MoTe 2 hetero-phase homojunctions remain to be accomplished, which requires precise control of thickness and careful protection from degradation. Second, to be compatible with the semiconductor industry, facile methods of constructing large-scale patterned MoTe 2 heterophase homojunction arrays are in demand. Lastly, MoTe 2 hetero-phase homojunctions involving the T d phase and other transient phases beyond need to be further explored.
Various challenges notwithstanding, 2D MoTe 2 hetero-phase homojunctions are expected to be a stepping stone to super-large-scale IC with extremely high integrity based on pure 2D materials, a fabulous platform for emerging physics research, as well as a promising candidate for future applications.